Filament ELEGOO PLA+ - 1kg oranžový 1,75mm
PLA+ filament pro 3D tisk - barva oranžová, průměr 1,75 mm, rozměrová přesnost ±0,02 mm, hmotnost 1 kg, materiál polylaktid plus s přísadami pro zvýšenou odolnost, vyšší odolnost proti praskání oproti standardnímu PLA, rovnoměrné navíjení na cívce, hladký povrch výtisků, nízké riziko ucpání trysky, vhodný pro FDM tiskárny
In stock 3 pcs
Expected shipping:
15.06.2026
Regular price
336,00 Kč
277,69 Kč
excl. VAT
Unit price
/
Unavailable
ELEGOO | SKU:
06444825
Filament ELEGOO PLA+ - 1kg oranžový 1,75mm
Regular price
336,00 Kč
277,69 Kč
excl. VAT
Unit price
/
Unavailable
Product description
ELEGOO filament in orange is a great choice for those looking for intense, well-saturated colors. The material has a smooth surface and provides high print details, which is well suited for prototypes and decorations. It is based on PLA+ (polylactide plus - a biodegradable material of plant origin, enriched with additives to increase durability). The spool contains 1 kg of filament.
Durability and precision
Thanks to increased resistance to cracking and better layer consistency, PLA+ is more durable than standard PLA, while still being just as easy to print from. The consistent diameter of 1.75 mm and dimensional accuracy of ± 0.02 mm guarantee a smooth material feed and less risk of clogging. Thanks to the smooth surface and good heat conduction, even more complex models come out cleanly and without deformation.
Convenience and compatibility
The material is wound evenly and checked manually, which reduces the risk of tangling. The entire package is vacuum-packed with a moisture absorber, so you can start printing immediately after opening. The product is suitable for most FDM (Fused Deposition Modeling) printers that support 1.75mm filament.
Technical parameters:
Color: Orange
Weight: 1 kg
Recommended printing settings:
Pre-print drying settings: 55 ± 5°C
Ambient temperature and humidity: ? 50°C, ? 20% relative humidity (storage with a desiccant)
Nozzle temperature: 200 - 230°C
Table temperature (depending on printer and surface): 35 - 65°C
Work surface type: Textured PEI (polyetherimide - a durable material that holds prints well) or other compatible plates.
Print speed: Less than 280 mm/s
Physical properties:
Density: 1.30 g/cm3
Melting point: 161°C
Deflection point under load: 56°C
Softening point (Vicat test): 63°C
Mechanical properties:
Tensile strength (XY - measured in the horizontal plane of the print, where the material is strongest): 38 ± 2 MPa
Elongation at break (XY): 7.9% ± 1.6%
Flexural strength (XY): 74 ± 4 MPa
Flexural modulus (XY): 2979 ± 156 MPa
Impact strength (XY): 65.5 ± 3.6 kJ/m2
Durability and precision
Thanks to increased resistance to cracking and better layer consistency, PLA+ is more durable than standard PLA, while still being just as easy to print from. The consistent diameter of 1.75 mm and dimensional accuracy of ± 0.02 mm guarantee a smooth material feed and less risk of clogging. Thanks to the smooth surface and good heat conduction, even more complex models come out cleanly and without deformation.
Convenience and compatibility
The material is wound evenly and checked manually, which reduces the risk of tangling. The entire package is vacuum-packed with a moisture absorber, so you can start printing immediately after opening. The product is suitable for most FDM (Fused Deposition Modeling) printers that support 1.75mm filament.
Technical parameters:
Color: Orange
Weight: 1 kg
Recommended printing settings:
Pre-print drying settings: 55 ± 5°C
Ambient temperature and humidity: ? 50°C, ? 20% relative humidity (storage with a desiccant)
Nozzle temperature: 200 - 230°C
Table temperature (depending on printer and surface): 35 - 65°C
Work surface type: Textured PEI (polyetherimide - a durable material that holds prints well) or other compatible plates.
Print speed: Less than 280 mm/s
Physical properties:
Density: 1.30 g/cm3
Melting point: 161°C
Deflection point under load: 56°C
Softening point (Vicat test): 63°C
Mechanical properties:
Tensile strength (XY - measured in the horizontal plane of the print, where the material is strongest): 38 ± 2 MPa
Elongation at break (XY): 7.9% ± 1.6%
Flexural strength (XY): 74 ± 4 MPa
Flexural modulus (XY): 2979 ± 156 MPa
Impact strength (XY): 65.5 ± 3.6 kJ/m2